Poly(epsilon-caprolactone)/corn starch blends containing 25, 50 and 75 wt.% starch were prepared by mechanical processing and characterized by the melt flow index (MFI), tensile test and scanning electron microscopy (SEM). For comparison, starch was used in gelatinized and nongelatinized forms and was also characterized by viscography. The addition of starch to poly(epsilon-caprolactone) reduced the MFI values, the tensile strength and the elongation at break, whereas the modulus increased. The reductions in the MFI and tensile properties were most evident when gelatinized starch was used. Viscography and SEM showed that starch was well gelatinized by the gelatinization process. Blends containing nongelatinized starch showed a good dispersion of starch but poor interfacial interactions.

A busca pela qualidade oriunda do processo de globalização emergente tem despertado o interesse de indústrias em solucionar os problemas ambientais. Neste trabalho, é apresentado o processo de reciclagem mecânica de resíduos industriais de poliuretano, incorporado em diferentes proporções em resinas poliuretanas. O processo de reciclagem foi desenvolvido levando-se em consideração o efeito da temperatura durante o processamento e as diferentes proporções (massa de resina nova: massa de resíduo -> 1:4, 1:8, 1:12,5, 1:20) dos resíduos incorporados na mistura. Os produtos obtidos em diferentes proporções foram caracterizados por meio das propriedades mecânicas de resistência à tração, resistência à abrasão, determinação da dureza e microscopia eletrônica de varredura (MEV), com o objetivo de avaliar a viabilidade de possíveis aplicações dos produtos desenvolvidos. Os resultados mostraram que foi possível reciclar proporções de até 1:20 com propriedades de resistência à tração, resistência à perda por abrasão e dureza adequadas para aplicação em pisos de academia de ginástica e pistas de atletismo.

The search for quality required in the globalization process has prompted industries to try and solve environmental problems. In this work, we present the mechanical recycling process of industrial polyurethane residues incorporated in different drifts in polyurethane resins. The recycling process was developed by considering conditions such as: effect of temperature in the process and the different proportions (mass of new resin: mass of residue -> 1:4, 1:8, 1:12.5, 1:20) of the residues incorporated in the mixture. The products obtained in different proportions were characterized by assessing their tensile stress properties, abrasion resistance, determination of hardness and using Scanning Electron Microscopy (SEM). The aim was to evaluate the viability of possible applications to the products originating from the recycling process. The results showed it to be possible to recycle proportions of up to 1:20 with mechanical properties, abrasion resistance, and hardness suitable for applications in tiles for floors in gymnasium and fitness centers.